生物降解材料聚乳酸－聚乙二醇共聚物體內(nèi)外降解 _

Degradation of Biodegradable Poly (DL-Lactic Acid)and Polyethyleneglycol Block Copolymer In Vivo and In Vitro

作者：王定國; 胡穎嘉; 鄭華; 吳增樹;

單位：四川省生物醫(yī)學(xué)材料監(jiān)測中心;

關(guān)鍵詞：聚乳酸－聚乙二醇共聚物; 聚乳酸; 體內(nèi)外降解;

分類號：

出版年·卷·期（頁碼）：1996·1·2（103-107）

摘要：

本文對ＤＬ－聚乳酸－聚乙二醇共聚物（ＰＥＬＡ）體內(nèi)外降解進行了研究。采用凝膠滲透色層法（ＧＰＣ）測定分子量，掃描電鏡（ＳＥＭ）觀察。ＰＥＬＡ在最初第５天出現(xiàn)降解，２月時分子量喪失體內(nèi)外分別為９７．２８％和９２．０％，而重量僅喪失８％。對其原因進行了討論，同時將ＰＥＬＡ與ＤＬ－聚乳酸（ＰＬＡ）進行了比較，探討分析了二者的降解機理。結(jié)果表明ＰＥＬＡ是一種新型生物降解材料。

The degradation of poly (DL-Lactic acid) and polyethyleneglycol block copolymer (PELA) was monitored in vitro and vivo. PELA degradation was observed in vivo at 5th day with scanning electron mioroscopy (SME), and molecular weight determined by gel permeation chromatography (GPC) showed a reduction to 97% after 8 weeks in vivo and 92% in vitro, whereas the mass loss change was 8% only. The causes were discussed, degradation of DL-PLA was studied in vitro and in vivo and was analyzed. The results showed that...

參考文獻：

中國期刊全文數(shù)據(jù)庫共找到 1 條

[1]	王定國，鄭華，胡穎嘉，邱書明. 降解材料聚乳酸－聚乙二醇生物相容性的研究[J]. 北京生物醫(yī)學(xué)工程, 1995,(03) .

服務(wù)與反饋：

【文章下載】【加入收藏】

提示：您還未登錄，請登錄！點此登錄

51黑料吃瓜在线观看,51黑料官网|51黑料捷克街头搭讪_51黑料入口最新视频